BMC jẹ ẹya abbreviation tiOlopobobo Molding yellowni ede Gẹẹsi, orukọ Kannada ni Bulk Molding Compound (tun npe ni: unsaturated poliesita gilasi okun fikun Bulk Molding Compound) nipasẹ awọn omi resini, kekere shrinkage oluranlowo, crosslinking oluranlowo, initiator, kikun, kukuru-ge gilasi okun flakes ati awọn miiran irinše ti awọn ti ara adalu eka, ninu awọn iwọn otutu ati titẹ awọn ipo, awọn crosslinking ti polyester ati polystyrated lenu waye. Labẹ iwọn otutu ati titẹ, polyester ti ko ni irẹwẹsi ati styrene jẹ ọna asopọ agbelebu ati imularada nipasẹ iṣesi polymerization. Awọn ohun-ini ẹrọ ti o dara julọ ati awọn ohun-ini itanna to dara julọ, ati resistance ooru ati awọn ohun-ini iṣelọpọ to dara ni lilo pupọ ni awọn ohun elo itanna, ohun elo, iṣelọpọ ọkọ ayọkẹlẹ, ọkọ ofurufu, gbigbe, awọn ile-iṣẹ ikole.
Eto agbekalẹ
1. Resini polyester ti ko ni itọrẹ: pẹlu smc / bmc resini pataki, nipataki m-phenyl soke, resistance resistance, ipata ipata, resistance arc, o dara fun iṣelọpọ ti Àkọsílẹ tabi awọn ọja anisotropic
2. Aṣoju Crosslinking; pẹlu monomer styrene, iye ti soke30% ~ 40%, ti o da lori akoonu ti awọn iwe ifowopamosi meji ninu polyester ti ko ni itọrẹ ati ipin ti awọn ifunmọ ilọpo meji ati awọn iwe ifowopamosi cis, ipin giga ti awọn monomers crosslinking, le gba imularada pipe diẹ sii.
3. Olupilẹṣẹ pẹlu oluranlowo imularada otutu ti o ga, tert-butyl peroxybenzoate (TBPB) jẹ ti aṣoju itọju otutu otutu ti o wọpọ julọ, iwọn otutu ibajẹ omi ti 104 iwọn otutu mimu ti 135 si awọn iwọn 160.
4. Low shrinkage oluranlowo commonly lo thermoplastic resini, awọn lilo ti ooru imugboroosi lati aiṣedeede soke ni ihamọ igbáti. Ni gbogbogbo, oṣuwọn idinku ti awọn ọja yẹ ki o ṣakoso ni 0.1 ~ 0.3%, nitorinaa iwọn lilo yẹ ki o wa ni iṣakoso muna.
5. Awọn ohun elo imudara: ni gbogbo igba ti a ti lo idapọ ti a ṣe ilana 6 ~ 12mm gun kukuru kukuru 6 ina retardant lilo Al2O3.3H2O-orisun, fifi kan kekere iye ti titun irawọ owurọ-ti o ni awọn ina retardant, hydrated alumina tun mu awọn ipa ti kikun 7. Fillers le din iye owo ti imudarasi awọn ohun-ini itanna ati idaduro ina. Kaboneti kalisiomu jẹ kikun ti a lo ti o gunjulo pẹlu iṣẹ gbogbogbo ti o dara, ni gbogbogbo ni irisi itanran, micropowder lẹhin itọju idapọ ati lẹhinna ṣafikun.
BMC ilana
1. San ifojusi si ọkọọkan ti fifi awọn ohun elo. Ti o dapọ ninu ẹrọ kneading iru-z, ẹrọ ilọpo ni ẹrọ alapapo, boya idapọpọ jẹ aṣọ le ṣe akiyesi lẹẹ awọ tabi awọ erogba ni iṣọkan ti o yẹ, nipa awọn iṣẹju 15 ~ 18
2. Gilaasi gilaasi kukuru kukuru lati darapọ mọ ti o kẹhin, ni kutukutu lati darapọ mọ nọmba nla ti awọn okun fifọ, ti o ni ipa lori agbara ti
3. Awọn ohun elo BMC gbọdọ wa ni ipamọ ni iwọn otutu kekere, ni gbogbogbo ni awọn iwọn 10 Celsius, iwọn otutu ga, resini ti ko ni itọrẹ jẹ rọrun lati ṣe agbelebu ati imularada, ati lẹhinna ṣiṣe awọn iṣoro mimu.
4. Iwọn otutu mimu: Awọn iwọn 140 tabi bẹ, iwọn otutu ti oke ati isalẹ 5 ~ 10 iwọn, titẹ titẹ 7mpa tabi bẹ, akoko idaduro 40 ~ 80s / mm
Ṣiṣe ayẹwo ile-iṣẹ
1. Ọja ọja: iṣoro fifọ ọja jẹ wọpọ, paapaa ni igba otutu awọn ipo otutu kekere. Ohun ti a npe ni fifọ n tọka si awọn ọja nipasẹ aapọn inu, ipa ti ita tabi awọn ipo ayika ati awọn ipa miiran lori aaye tabi awọn dojuijako inu.
2. Solusan; pataki lati awọn ohun elo aise, ipin ati ilana lati yanju.
2.1 Aṣayan ati sisẹ awọn ohun elo aise
1) Resini jẹ matrix ti bmc, resini polyester ti ko ni itọrẹ, ester fainali,phenolic resini, melamine, bbl Resini jẹ imularada ọja, pẹlu agbara ipilẹ. Nitorina, lilo ti smc / bmc pataki resini, jẹ m-phenylene iru resini, m-phenylene resini ju awọn o-phenylene iru ti ga viscosity, ki ni afikun si awọn resini ara shrinkage jẹ kekere, le gba diẹ crosslinking monomers, ki awọn iwuwo ti awọn iwuwo posi, isunki oṣuwọn dinku.
(2) ṣafikun aṣoju isunki kekere apapo; unsaturated polyester resin curing contraction rate of up to 5 ~ 8%, fi kan orisirisi ti filler isunki jẹ ṣi siwaju sii ju 3%, awọn ọja gbogbo isunki oṣuwọn ti diẹ ẹ sii ju 0.4% lati kiraki, ki fi thermoplastic resins, awọn lilo ti thermoplastic resins lati se imukuro gbona imugboroosi ti awọn curing ihamọ ti awọn ẹya ara. pmma, ps add ati monomer styrene dapọ ati itu ti o dara julọ, afikun ti pmma Ipari naa dara julọ. Ilọkuro ọja le jẹ iṣakoso ni 0.1 ~ 0.3%.
(3) kikun, ina retardant, gilasi okun; gilaasi gilaasi gigun - gbogbo 6 ~ 12mm, nigbakan lati pade awọn ohun-ini ẹrọ giga si 25mm; ni ibere lati pade awọn ibeere ti igbáti fluidity, to 3mm. akoonu okun gilasi nigbagbogbo jẹ 15% ~ 20%; fun awọn ọja iṣẹ ṣiṣe giga, si 25%. Akoonu okun gilasi BMC kere ju SMC, o le ṣafikun kikun diẹ sii, nitorinaa idiyele naa dinku lati le ṣe kikun inorganic. Isalẹ lati le ṣe kikun inorganic, retardant ina, gilaasi fiber ati resini ni apapo kemikali laarin lilo gbogbogbo ti itọju silane coupling agent ṣaaju ki o to dapọ, ti a lo nigbagbogbo KH-560, ipa KH-570 dara lati darapọ mọ awọn ipilẹ ti o dara, awọn ohun elo micronized, gẹgẹ bi awọn carbonate kalisiomu ti o wuwo pẹlu iwọn micronized, qui patiku 12 ~ 570 (12 ~ 570)
2.2 BMC proportioning awọn ibeere Bmc mimọ resini, iye ko le jẹ kere ju 20%, awọn oniwe-iye ti initiator jẹmọ si iye ti crosslinking oluranlowo besikale ko ni lati afikun ohun ti fi awọn iye ti crosslinking oluranlowo ninu awọn resini akoonu kà fun 35%, ni afikun si awọn iye ti kekere shrinkage oluranlowo lati da tun da lori iye ti resini. Awọn lilo ti ga-otutu curing oluranlowo TBPB, kikun ati ina retardant (aluminiomu hydroxide) lati da awọn lapapọ iye ti nipa 50% jẹ diẹ yẹ, jẹ lemeji bi awọn resini, ju Elo lati da awọn agbara ti awọn be ti bajẹ, rọrun lati kiraki!
2.3 Production ilana awọn ipo
(1)dapo, lakokọ, nigba ti a ba dapọ ohun elo ti a o fi dapọ boṣeyẹ, erupẹ naa kọkọ fi walẹ kekere kan pato, lẹhinna fi omi ṣan nla kan, ao da omi naa akọkọ ati lẹhinna fi kun, olupilẹṣẹ ni ikẹhin lati fi kun, a gbọdọ fi awọn ohun elo ti o nipọn sii ṣaaju ki o to pasini resin ati polystyrene kneading. Okun gilasi ti wa ni afikun ni awọn ipele
(2) awọn ipo ilana imudọgba: awọn ilana ilana idọgba taara ni ipa lori ọja naa dara tabi buburu. Nigbagbogbo pẹlu ilosoke ti titẹ mimu, idinku dinku. Iwọn otutu mimu ti o ga julọ yoo ṣe laini idapọ dada, ohun elo ko jẹ aṣọ, aapọn inu inu yatọ, rọrun lati kiraki. Idaduro titẹ fun itẹsiwaju ti o yẹ fun akoko jẹ itọsi si idena ti fifọ awọn ẹya.
(3) eto idabobo preheating: awọn ẹya iwọn otutu kekere jẹ rọrun lati kiraki. Nitorina, awọn ohun elo yẹ ki o wa ni preheated